Formula date: Jun 7, 2024
Component
F420/GB963B-100/HT600.
Curing method
Self-drying.
Application
Leading edge protection adhesive for wind turbine blades.
Characters
Fast-drying, low VOC, rain erosion resistance, high strength and high elongation.
A component
| Material | Content |
|---|---|
| F420(Desmophen NH 1420 Equivalent) | 45 |
| BYK163 dispersant | 1 |
| Rutile titanium dioxide | 32 |
| 3A molecular sieve | 3 |
| 1250-mesh barium sulfate | 15 |
| BYK-AF bentonite | 0.8 |
| BYK-R606 rheology enhancer | 0.5 |
| BYK410 rheology agent | 0.1 |
| BYK085 defoamer | 0.2 |
| BYK1790 defoamer | 0.3 |
| EFKA3600 leveling agent | 0.1 |
| n-butyl ester | 2 |
B component
| Material | Content |
|---|---|
| GB963B-100(Desmodur E30700 (E2863XP) Equivalent) | 90 |
| HT600 | 10 |
Ratio
A:B=100:60 by weight
Specifications
| Pot life | >20min |
| Mixed solid content | ≥98% |
| Touch dry time 25℃ | ≤1h |
| Hard dry time 25℃ | ≤4h |
| Aging resistance | >3000h |
| Rain erosion resistance | ≥4h |
| Elongation | >200% |
| Tensile strength | >20Mpa |
Feiyang Protech has been specializing in the production of raw materials for polyaspartic coatings for 30 years and can provide polyaspartic resins, hardeners and coating formulations. Feel free to contact us: [email protected]
Our products list:
- Polyaspartic Resin
- Isocyanate Hardener
- Epoxy Hardener
- Polyaspartic Coating Formulation showcase cases
Consult our engineers to customize a coating formulation for your project. Contact our Tech Team